ADHESIVES |
| 配方說(shuō)明： |
High Heat Resistant Adhesives |
| 配方組成： |
Methylethyl Ketone/-
Part B
"Neoprene" AD-20/-
Hexane/-
Hexane/-
Zinc Oxide/5.0
"Neoprene" AD-30/-
"Neoprene" AD-20/50.0
"Neoprene" AC/50.0
"Maglite" D/4.0
Zinc Oxide/5.0
"Agerite" Resin D/2.0
"Neoprene" AC/-
Toluene/111.0
Methylethyl Ketone/111.0
Hexane/111.0
"Agerite" Resin D/2.0
"Neoprene" AD-30/100.0
"SP-154"/45.0
"Maglite" D/4.5
Water/2.0
Toluene/16.0
"SP-154"/45.0
Methylethyl Ketone/16.0 |
| 配制方法： |
To obtain optimum heat resistance, Part A should be mixed in the conventional manner on a rubber mill, and then dissolved in the solvent system shown under "A." Part B, the resin and "Maglite" D, should be dissolved in the water and solvent system, and pre-reacted for a minimum of 6 hours prior to blending with Part A.
use of "SP-154" will result in excellent heat resistance, as well as a completely non-phasing formulation. "SP-155" will produce formulations with heat resistance slightly less than "SP-154," but with longer open-time. Its phase resistance, while excellent, is not as good as SP-154. |
|